Effects of grape seed extract on the properties of pullulan polysaccharide/xanthan gum active films for apple...

Grape seed extract (GSE) was added to pullulan polysaccharide (PP)/xanthan gum (XG) as composite film (PP/XG/GSE or PXG). The observed composite morphology indicated their biocompatibility. Sample PXG100 (contain 100 mg/L GSE) demonstrated the best mechanical properties, with tensile strength of 16.62 ± 1.27 MPa, and the elongation at break of (22.60 ± 0.48)%. The 2,2-diphenyl-1-picrylhydrazyl (DPPH) and 2,2'-azino-bis-(3-ethylbenzothiazoline-6-sulphonic acid) (ABTS) radical scavenging activity of PXG150 were the highest at (81.52 ± 1.57)% and (90.85 ± 1.54)%, respectively. PXG films also demonstrated inhibitory effects on Staphylococcus aureus, Escherichia coli, and Bacillus subtilis. The PXG films could also prolong the shelf life of fresh-cut apples because it could decrease the rate of weight loss and retain more vitamin C and total polyphenol even on the 5^th day. The weight loss rate of PXG150 was decreased from (8.58 ± 0.6)% (control) to (4.15 ± 0.19)%. It was able to achieve vitamin C and total polyphenol retention rate of 91 % and 72 %, respectively, which was significantly higher that the control sample. Therefore, GSE had contributed in enhancing the antibacterial, antioxidant properties, mechanical strength, UV protection and water resistance in PXG composite films. This effectively extend the shelf life of fresh-cut apples, which it will be an excellent food packaging material.