The effect of dentin surface pretreatment using dimethyl sulfoxide on the bond strength of a universal bonding agent...

This study aimed to evaluate the effect of dentin pretreatment by Dimethyl Sulfoxide (DMSO) on the bond strength and microleakage of a universal bonding agent to dentin.

Fifty-six dentinal discs (thickness = 2 mm) were obtained from the crowns of the human third molars. The disks were assigned into 4 groups and treated as follows; self-etch-control group: G-Premio universal adhesive was used in self-etch mode, total-etch-control: G-Premio universal adhesive was used in total-etch mode, self-etch-DMSO: Water-based DMSO (50% volume) was applied on the samples for 60 s followed by application of G-Premio universal adhesive in self-etch mode, and Total-etch-DMSO: The samples were etched, and then, water-based DMSO was applied on them for 60 s followed by the application of G-Premio universal adhesive in total-etch mode. Afterward, resin composite was placed on all samples and light-cured. The samples were kept in distilled water and subjected to 5000 thermal cycles. Microshear bond strength was measured using the universal testing machine and failure modes were analyzed using a stereomicroscope. Forty-eight human third molars were used for microleakage evaluation and a standardized class five cavity was prepared on the buccal surface of each tooth. The teeth were assigned into 4 groups and received aforementioned surface treatment and the cavities were filled with resin composite. After storing in water for 24 h, the samples were subjected to 5000 cycles of thermocycling and the microleakage level of the samples was evaluated using silver nitrate uptake at the bonded interface. Two-way ANOVA test was used to analyze the effect of bonding technique (self-etch/ total-etch) and DMSO pretreatment on the microshear bond strength and microleakage of G-Premio adhesive to dentin.

Bonding technique had no effect on the bond strength values (p = 0.17) while DMSO pretreatment significantly decreased the microshear bond strength of the samples (p = 0.001). DMSO application increased microleakage significantly in total-etch (P-value = 0.02) while it had no effect in self-etch mode (P-value = 0.44).

Pretreatment of dentin using 50% DMSO significantly reduced the bond strength of G-Premio Bond in both self-etch and total-etch modes. DMSO effect on microleakage depended on the etching technique; DMSO increased the microleakage level when the adhesive was used in total-etch mode while did not affect the microleakage in self-etch mode.