Biological properties of Ceraputty as a retrograde filling material: an in vitro study on hPDLSCs
Sergio López-García1, Francisco J Rodríguez-Lozano2, José Luis Sanz3,4
1Departament d'Estomatologia, Facultat de Medicina I Odontologia, Universitat de València, 46010, Valencia, Spain.
Objectives:
To assess the cytocompatibility and bioactive potential of the new calcium silicate-based cement Ceraputty on human periodontal ligament stem cells (hPDLSCs) compared to Biodentine and Endosequence BC root repair material (ERRM).
Materials And Methods:
hPDLSCs were isolated from extracted third molars from healthy donors. Standardized sample discs and 1:1, 1:2, and 1:4 eluates of the tested materials were prepared. The following assays were performed: surface element distribution via SEM-EDX, cell attachment and morphology via SEM, cell viability via a MTT assay, osteo/cemento/odontogenic marker expression via RT-qPCR, and cell calcified nodule formation via Alizarin Red S staining. hPDLSCs cultured in unconditioned or osteogenic media were used as negative and positive control groups, respectively. Statistical analysis was performed using one-way ANOVA or two-way ANOVA and Tukey's post hoc test. Statistical significance was established at p < 0.05.
Results:
The highest Ca2+ peak was detected from Biodentine samples, followed by ERRM and Ceraputty. hPDLSC viability was significantly reduced in Ceraputty samples (p < 0.001), while 1:2 and 1:4 Biodentine and ERRM samples similar results to that of the negative control (p > 0.05). Biodentine and ERRM exhibited an upregulation of at least one cemento/odonto/osteogenic marker compared to the negative and positive control groups. Cells cultured with Biodentine produced a significantly higher calcified nodule formation than ERRM and Ceraputty (p < 0.001), which were also higher than the control groups (p < 0.001).
Conclusion:
Ceraputty evidenced a reduced cytocompatibility towards hPDLSCs on its lowest dilutions compared to the other tested cements and the control group. Biodentine and ERRM promoted a significantly higher mineralization and osteo/cementogenic marker expression on hPDLSCs compared with Ceraputty. Further studies are necessary to verify the biological properties of this new material and its adequacy as a retrograde filling material.
Clinical Relevance:
This is the first study to elucidate the adequate biological properties of Ceraputty for its use as a retrograde filling material.