Nitrogen doped bimetallic sludge biochar composite for synergistic persulfate activation: Reactivity, stability and...

As a recycling use of waste activated sludge (WAS), we used high-temperature pyrolysis of WAS to support bimetallic Fe-Mn with nitrogen (N) co-doping (FeMn@N-S), a customized composite catalyst that activates peroxysulphate (PS) for the breakdown of tetracycline (TC). First, the performance of TC degradation was evaluated and optimized under different N doping, pH, catalyst dosages, PS dosages, and contaminant concentrations. Activating PS with FeMn@N-S caused the degradation of 91% of the TC in 120 min. Next, characterization of FeMn@N-S by XRD, XPS and FT-IR analysis highlights N doping is beneficial to take shape more active sites and reduces the loss of Fe and Mn during the degradation reaction. As expected, the presence of Fe-Mn bimetallic on the catalyst surface increases the rate of electron transfer, promoting the redox cycle of the catalyst. Other functional groups on the catalyst surface, such as oxygen-containing groups, accelerated the electron transfer during PS activation. Free radical quenching and ESR analysis suggest that the main contributor to TC degradation is surface-bound SO₄^•-, along with the presence of single linear oxygen (¹O₂) oxidation pathway. Finally, the FeMn@N-S composite catalyst exhibits excellent pH suitability and reusability, indicating a solid practicality of this catalyst in PS-based removal of antibiotics from wastewater.