Surface Equilibration Mechanism Controls the Stability of a Model Codeposited Glass Mixture of Organic Semiconductors

While previous work has identified the conditions for preparing ultrastable single-component organic glasses by physical vapor deposition (PVD), little is known about the stability of codeposited mixtures. Here, we prepared binary PVD glasses of organic semiconductors, TPD (N,N'-Bis(3-methylphenyl)-N,N'-diphenylbenzidine) and m-MTDATA (4,4',4″-Tris[phenyl(m-tolyl)amino]triphenylamine), with a 50:50 mass concentration over a wide range of substrate temperatures (T_sub). The enthalpy and kinetic stability are evaluated with differential scanning calorimetry and spectroscopic ellipsometry. Binary organic semiconductor glasses with exceptional thermodynamic and kinetic stability comparable to the most stable single-component organic glasses are obtained when deposited at T_sub = 0.78-0.90T_g (where T_g is the conventional glass transition temperature). When deposited at 0.94T_g, the enthalpy of the m-MTDATA/TPD glass equals that expected for the equilibrium liquid at that temperature. Thus, the surface equilibration mechanism previously advanced for single-component PVD glasses is also applicable for these codeposited glasses. These results provide an avenue for designing high-performance organic electronic devices.