Large-Scale Preparation of Carboxylated Cellulose Nanocrystals and Their Application for Stabilizing Pickering...

Cellulose nanocrystals (CNCs) with varied unique properties have been widely used in emulsions, nanocomposites, and membranes. However, conventional CNCs for industrial use were usually prepared through acid hydrolysis or heat-controlled methods with sulfuric acid. This most commonly used acid method generally suffers from low yields, poor thermal stability, and potential environmental pollution. Herein, we developed a high-efficiency and large-scale preparation strategy to produce carboxylated cellulose nanocrystals (Car-CNCs) via carboxymethylation-enhanced ammonium persulfate (APS) oxidation. After carboxymethylation, the wood fibers could form unique "balloon-like" structures with abundant exposed hydroxy groups, which facilitated exfoliating fibril bundles into individual nanocrystals during the APS oxidation process. The production process under controlled temperature, time period, and APS concentrations was optimized and the resultant Car-CNCs exhibited a typical structure with narrow diameter distributions. In particular, the final Car-CNCs exhibited excellent thermal stability (≈346.6 °C) and reached a maximum yield of 60.6%, superior to that of sulfated cellulose nanocrystals (Sul-CNCs) prepared by conventional acid hydrolysis. More importantly, compared to the common APS oxidation, our two-step collaborative process shortened the oxidation time from more than 16 h to only 30 min. Therefore, our high-efficiency method may pave the way for the up-scaled production of carboxylated nanocrystals. More importantly, Car-CNCs show potential for stabilizing Pickering emulsions that can withstand changeable environments, including heating, storage, and centrifugation, which is better than the conventional Sul-CNC-based emulsions.