Reactive Janus Particle Compatibilizer with Adjustable Structure and Optimal Interface Location for Compatibilization...

Highly immiscible blend materials with distinctive and excellent properties play a key role in meeting the application needs, especially in extreme environments, and reactive nanoparticles are used to increase the interface adhesion and optimize the morphology of highly immiscible blending. However, these reactive nanoparticles tend to aggregate and even agglomerate during reactive blending, which significantly deteriorates their compatibilization efficiency. Herein, reactive Janus particles with the epoxy group and various siloxane molecular long chain grafting ratios (E-JP-PDMS) were synthesized using SiO₂@PDVB Janus particles (JP) and used as compatibilizers for polyamide and methyl vinyl silicone elastomer (PA/MVQ) blends, which were highly immiscible. The effects of the structure of E-JP-PDMS Janus nanoparticles on their location at the interfaces between the PA and MVQ as well as their compatibilization efficiency for the PA/MVQ blends were investigated. The location and dispersion of E-JP-PDMS at the interfaces were improved by increasing the PDMS content in E-JP-PDMS. The average diameter of the MVQ domains of the PA/MVQ (70/30, w/w) was 79.5 μm and was reduced to 5.3 μm in the presence of 3.0 wt % of the E-JP-PDMS with 65 wt % PDMS. As a comparison, it was 45.1 μm in the presence of 3.0 wt % of a commercial compatibilizer (ethylene-butylacylate-maleic anhydride copolymer, denoted as EBAMAH), which provides a guideline for the design and preparation of efficient compatibilizers for highly immiscible polymer blends.