One-Step Bulk-Suspension Polymerization of Polyethylene Glycol-Based Copolymer Microspheres for Phase Change Textiles

The paper presents a feasible strategy through one-step bulk-suspension polymerization, grafting PEG onto an in situ synthesized copolymer. In more detail, PEG was grafted onto a homemade polystyrene/maleic anhydride copolymer (SMA) via bulk-suspension polymerization with poly(vinyl alcohol) as a suspending agent. According to the optimal reaction conditions, the grafting rate of PEG was 56.2% through chemical titration experiments. At the same time, the quantitative relationship between the grafting rate and enthalpy was demonstrated for the first time in a PEG-based solid-solid phase change material (S-SPCM). Morphology observation revealed that the obtained S-SPCM is made up of white microspheres of approximately 100-150 μm. The powdery product polystyrene/maleic anhydride grafted polyethylene glycol (SMA-g-PEG) obtained through bulk-suspension polymerization endowed that the whole product could be used directly as a phase change material without postprocessing. The melting enthalpy and crystallization enthalpy of SMA-g-PEG were 79.3 J/g and 76.9 J/g, respectively. Based on the effective fixed load of PEG, the macrostructure of SMA-g-PEG was almost unchanged at 70 °C compared with the macrostructures at 20 °C, and the latent heat of SMA-g-PEG was decreased slightly after 1000 thermal cycles. Overall, the obtained SMA-g-PEG can be used as a filler in insulation materials and composited with fibers to obtain phase change thermoregulated smart textiles.