Effect of Whitening Toothpastes with Different Active Agents on the Abrasive Wear of Dentin Following Tooth Brushing...

The aim of this research was to evaluate the abrasive dentin wear that can be induced by three commercial whitening toothpastes following a tooth-brushing simulation (TBS) corresponding to a three-month period. Sixty human canines were selected, and the roots were separated from the crowns. Then the roots were randomly divided into six groups (n = 10) and were submitted to TBS using the following slurries: Group 1-deionized water (RDA = 5); Group 2-ISO dentifrice slurry (RDA = 100); Group 3-a regular toothpaste (RDA = 70); Group 4-a charcoal-containing whitening toothpaste; Group 5-a whitening toothpaste containing blue covasorb and hydrated silica; and Group 6-a whitening toothpaste containing microsilica. Following TBS, surface loss and surface roughness changes were evaluated using confocal microscopy. Additionally, surface morphology and mineral content changes were observed using scanning electron microscopy and energy-dispersive X-ray spectroscopy. The deionized water group presented the lowest surface loss (p < 0.05), while the charcoal-containing toothpaste presented the highest surface loss, followed by ISO dentifrice slurry (p < 0.001). Blue-covasorb-containing and regular toothpastes did not present statistically significant differences (p = 0.245), and neither didmicrosilica-containing toothpaste or ISO dentifrice slurry (p = 0.112). The surface height parameters and surface morphology changes of the experimental groups followed the surface loss patterns, while no differences were detected in mineral content after TBS.Although the charcoal-containing toothpaste exhibited the highest abrasive wear to dentin, according to ISO 11609, all the tested toothpastes exhibited appropriate abrasive behavior towards dentin.