Impact of a Novel Phosphoramide Flame Retardant on the Fire Behavior and Transparency of Thermoplastic Polyurethane...

In many application fields of thermoplastic polyurethane (TPU), excellent flame retardancy and transparency are required. However, higher flame retardancy is often at the expense of transparency. It is difficult to achieve high flame retardancy while maintaining the transparency of TPU. In this work, a kind of TPU composite with good flame retardancy and light transmittance was obtained by adding a new synthetic flame retardant named DCPCD, which was synthesized by the reaction of diethylenetriamine and diphenyl phosphorochloridate. Experimental results showed that 6.0 wt % DCPCD endowed TPU with a limiting oxygen index value of 27.3%, passing the UL 94 V-0 rating in the vertical burning test. The cone calorimeter test results showed that the peak heat release rate (PHRR) of the TPU composite was dramatically reduced from 1292 kW/m² (pure TPU) to 514 kW/m² by adding only 1 wt % DCPCD. With the increase of DCPCD contents, the PHRR and total heat release gradually decreased, and the char residue gradually increased. More importantly, the addition of DCPCD has little effect on the transparency and haze of TPU composites. In addition, scanning electron microscopy, Raman spectroscopy, and X-ray photoelectron spectroscopy were carried out to investigate the morphology and composition of the char residue for TPU/DCPCD composites and explore the flame retardant mechanism of DCPCD in TPU.