Controlled p-Type Doping of Pyrite FeS₂

Pyrite FeS₂ has extraordinary potential as a low-cost, nontoxic, sustainable photovoltaic but has underperformed dramatically in prior solar cells. The latter devices focus on heterojunction designs, which are now understood to suffer from problems associated with FeS₂ surfaces. Simpler homojunction cells thus become appealing but have not been fabricated due to the historical inability to understand and control doping in pyrite. While recent advances have put S-vacancy and Co-based n-doping of FeS₂ on a firm footing, unequivocal evidence for bulk p-doping remains elusive. Here, we demonstrate the first unambiguous and controlled p-type transport in FeS₂ single crystals doped with phosphorus (P) during chemical vapor transport growth. P doping is found to be possible up to at least ∼100 ppm, inducing ∼10¹⁸ holes/cm³ at 300 K, while leaving the crystal structure and quality unchanged. As the P doping is increased in crystals natively n-doped with S vacancies, the majority carrier type inverts from n to p near ∼25 and ∼55 ppm P, as detected by Seebeck and Hall effects, respectively. Detailed temperature- and P-doping-dependent transport measurements establish that the P acceptor level is 175 ± 10 meV above the valence band maximum, explain details of the carrier inversion, elucidate the relative mobility of electrons and holes, reveal mid-gap defect levels, and unambiguously establish that the inversion to p-type occurs in the bulk and is not an artifact of hopping conduction. Such controlled bulk p-doping opens the door to pyrite p-n homojunctions, unveiling new opportunities for solar cells based on this extraordinary semiconductor.