Study on injectable silver-incorporated calcium phosphate composite with enhanced antibacterial and biomechanical...

Although commonly used in orthopedic surgery, bone cements often face a high risk of post-operative infection. Developing bone cement with antibacterial capability is an effective path for eliminating implant-associated infections. Herein, the potential of silver ions (Ag+) and silver nanoparticles (AgNPs) in modifying CPC for long-term antibacterial property was investigated. Ag+ ions or AgNPs of various concentrations were incorporated in starch-modified calcium phosphate bone cement (CPB) to obtain Ag+-containing (Ag+@CPB) and AgNPs-containing (AgNP@CPB) bone cements. The results showed that all silver-containing CPBs had setting times of about 25-40 min, compressive strengths of greater than 22 MPa, high cytocompatibility but inhibitory effect on Staphylococcus aureus growth. After soaking for 1 week, the mechanical properties and the cytocompatibility of all cements revealed no significant changes, but only CPB with a relatively high content of Ag+ (H-Ag+@CPB) maintained good antibacterial capability over the tested time period. In addition, all the cements showed high injectability and interdigitating capability in cancellous bone and demonstrated augmentation effect on the cannulated pedicle screws fixation in the Sawbones model. In summary, the sustainable antibacterial capability and enhanced biomechanical properties demonstrated that Ag+ ions were more suitable for the fabrication of antibacterial CPC compared to AgNPs. Also, the H-Ag+@CPB, with good injectability, high cytocompatibility, good interdigitating and biomechanical property in cancellous bone, and sustainable antibacterial effects, bears great potential for the treatments of bone infections or implant-associated infections.