Structural and performance variation of PES/PVDF membranes after exposure to the pretreated feed water of CECs

In this study, the removal efficiency of chemicals of emerging concerns (CECs) was evaluated under exposure to various doses of UV/H2O2-based oxidation processes in combination with membrane filtration for three cleaning cycles. Polyethersulphone (PES) and polyvinylidene fluoride (PVDF) materials based membranes were used for this study. The chemical cleaning of the membranes was performed by immersion of the membranes into 1 N HCl followed by adding 3000 mg.L-1 NaOCl for 1hr. Degradation and filtration performance was evaluated using Liquid Chromatography with tandem mass spectrometry (LC-MS/MS) and total organic carbon (TOC) analysis. Membrane fouling analysis for assessing the comparative performance of PES and PVDF membranes was determined by specific fouling and fouling indices evaluation. Membrane characterization results show that the alkynes and carbonyl group formation are due to dehydrofluorination and oxidation of PVDF and PES membranes under the attack of foulants and cleaning chemicals, which resulted in a reduction of fluoride percentage and an increase in sulfur percentage in the PVDF and PES membranes. A decrease in the hydrophilicity of the membranes in underexposed conditions was observed and is consistent with an increase in dose. Degradation results of CECs follow with the highest removal efficiency of chlortetracycline (CTC) followed by atenolol (ATL), acetaminophen (ACT), and caffeine (CAF) degradation due to attack on the aromatic ring and the carbonyl group of CECs by OH exposure. Membrane exposed at 3 mg.L-1 dose of UV/H2O2-based CECs shows minimum alteration with higher filtration efficiency and lower fouling, particularly in PES membranes.