Solar energy is an inexhaustible clean energy providing a key solution to the dual challenges of energy and environmental crises. Graphite-like layered molybdenum disulfide (MoS2) is a promising photocatalytic material with three different crystal structures, 1T, 2H and 3R, each with distinct photoelectric properties. In this paper, 1T-MoS2 and 2H-MoS2, which are widely used in photocatalytic hydrogen evolution, were combined with MoO2 to form composite catalysts using a bottom-up one-step hydrothermal method. The microstructure and morphology of the composite catalysts were studied by XRD, SEM, BET, XPS and EIS. The prepared catalysts were used in the photocatalytic hydrogen evolution of formic acid. The results show that MoS2/MoO2 composite catalysts have an excellent catalytic effect on hydrogen evolution from formic acid. By analyzing the photocatalytic hydrogen production performance of composite catalysts, it suggests that the properties of MoS2 composite catalysts with different polymorphs are distinct, and different content of MoO2 also bring differences. Among the composite catalysts, 2H-MoS2/MoO2 composite catalysts with 48% MoO2 content show the best performance. The hydrogen yield is 960 µmol/h, which is 1.2 times pure 2H-MoS2 and two times pure MoO2. The hydrogen selectivity reaches 75%, which is 22% times higher than that of pure 2H-MoS2 and 30% higher than that of MoO2. The excellent performance of the 2H-MoS2/MoO2 composite catalyst is mainly due to the formation of the heterogeneous structure between MoS2 and MoO2, which improves the migration of photogenerated carriers and reduces the possibilities of recombination through the internal electric field. MoS2/MoO2 composite catalyst provides a cheap and efficient solution for photocatalytic hydrogen production from formic acid.