Construction of High Quantum Yield Lanthanide Luminescent MOF Platform by In Situ Doping and Its Temperature Sensing
Shiying Liu1, Wei Liu2, Yiliang Sun2
1Key Laboratory of Nonferrous Metals Chemistry and Resources Utilization of Gansu Province, State Key Laboratory of Applied Organic Chemistry and College of Chemistry and Chemical Engineering, Lanzhou University, 730000 Lanzhou, China.
Abstract:
Lanthanide luminescent MOF materials show excellent luminescent properties. However, obtaining lanthanide luminescent MOFs with high quantum yield is a challenging research. A novel bismuth-based metal-organic framework [Bi(SIP)(DMF)2] was constructed by solvothermal method, utilizing 5-sulfoisophthalic acid monosodium salt (NaH2SIP) and Bi(NO3)3·5H2O. Thereafter, doped MOFs (Ln-Bi-SIP, Ln = Eu, Tb, Sm, Dy, Yb, Nd, Er) with different luminescent properties have been obtained by in situ doping with different lanthanide metal ions, among which Eu-Bi-SIP, Tb-Bi-SIP, Sm-Bi-SIP, and Dy-Bi-SIP have high quantum yield. What is special is that the doping amount of Ln3+ ions is very low, and the doped MOF can achieve high luminescence quantum yields. EuTb-Bi-SIP obtained by Eu3+/Tb3+ codoping and Dy-Bi-SIP exhibit good temperature sensing performance over a wide temperature range with the maximum sensitivity Sr of 1.6%·K-1 (433 K) and 2.6%·K-1, respectively (133 K), while the cycling experiments also show good repeatability in the assay temperature range. Finally, considering the practical application value, EuTb-Bi-SIP was blended with an organic polymer poly(methyl methacrylate) (PMMA) to produce a thin film, which shows different color changes at different temperatures.