Investigating the effect of solid loading on microstructure, mechanical properties, and translucency of highly
Li Wang1, Hang Yu1, Zongdong Hao1
1Jiangsu Key Laboratory of Advanced Food Manufacturing Equipment and Technology, School of Mechanical Engineering, Jiangnan University, Wuxi, 214122, Jiangsu, China; Institute of Advanced Technology, Jiangnan University, Wuxi, 214122, Jiangsu, China.
Abstract:
A study was conducted to explore the potential of 5 mol% yttria-partially stabilized zirconia (5Y-PSZ) ceramics for dental restorations, using stereolithography (SLA) printing technique. Four different solid loadings were established in the ceramic paste systems to study their effects on microstructure, mechanical properties, and translucency. The study examined the rheological behavior and photopolymerization performance of the ceramic pastes with varying solid loadings. Results showed that, an increase in powder concentration resulted in a decrease in cure depth (Cd) and penetration depth (Dp). A narrower pore size distribution was observed in the green bodies with a high solid loading, facilitating the achievement of final densification. The green and sintered densities were highest at 52 vol%, with values of 3.46 ± 0.01 g/cm3 and 6.01 ± 0.02 g/cm3, respectively. Additionally, all of the green strengths exceeded 30 MPa, with a maximum of 35.09 ± 2.02 MPa obtained at 44 vol%. The maximum flexural strength and minimum contrast ratio (CR) value of 746 ± 75 MPa and 0.40 ± 0.01 were achieved at 52 vol% after sintering. No significant differences were observed in the phase composition and hardness of the as-sintered ceramics. Though significant differences were observed in photopolymerization performance, four materials showed similar structural reliability considering Weibull modulus and characteristic strength.