Red mud-derived iron carbon catalyst for the removal of organic pollutants in wastewater

In order to reduce the environmental hazards of red mud (RM) and realize its resource utilization, in this study, RM-based iron-carbon micro-electrolysis material (RM-MEM) were prepared by a carbothermal reduction process using RM as raw material. The influence of the preparation conditions on the phase transformation and structural characteristics of the RM-MEM were investigated during the reduction process. The ability of RM-MEM to remove organic pollutants from wastewater was evaluated. The results showed that RM-MEM prepared at a reduction temperature of 1100 °C, a reduction time of 50 min and a coal dosage of 50% had the best removal effect for the degradation of methylene blue (MB). When the initial MB concentration was 20 mg L^-1, the amount of RM-MEM material was 4 g L^-1, the initial pH was 7, and the degradation efficiency reached 99.75% after 60 min. When RM-MEM is split into carbon free and iron free parts for use, the degradation effect becomes worse. Compared to other materials, RM-MEM has lower cost and better degradation. X-ray diffraction (XRD) analysis showed that hematite was transformed to zero-valent iron with the increase in the roasting temperature. Scanning electron microscopy (SEM) and energy spectroscopy (EDS) analysis showed that micron-sized ZVI particles were formed in the RM-MEM, and increasing the carbon thermal reduction temperature was beneficial to the growth of zero-valent iron particles.