Efficient preparation of high-purity cellulose from moso bamboo by p-toluenesulfonic acid pretreatment
Related Experiment Video
Updated: Jul 26, 2025
Towards Biomimicking Wood: Fabricated Free-standing Films of Nanocellulose, Lignin, and a Synthetic Polycation
Published on: June 17, 2014
Bin Wang1, Xuan Zhang2, Jinpeng Li1
1Plant Fiber Material Science Research Center, State Key Laboratory of Pulp and Paper Engineering, School of Light Industry and Engineering, South China University of Technology, Guangzhou 510640, China; Guangdong Provincial Key Laboratory of Plant Resources Biorefinery, Guangzhou 510006, China.
Abstract:
This work proposed a promising biorefinery method for the deconstruction of moso bamboo by using p-toluenesulfonic acid (P-TsOH) pretreatment to product high-purity cellulose (dissolving pulp). The cellulose pulp with high α-cellulose content (82.36 %) was successfully prepared for 60 min at low pretreatment temperature (90 °C) and atmospheric pressure. After the simple bleaching and cold caustic extraction (CCE) processes, the properties of cellulose pulp, such as α-cellulose content, polymerization, ISO brightness, all met the standard of dissolving pulp. In general, the cooking method through P-TsOH pretreatment can shorten the preparation time, which can effectively reduce energy consumption and chemical consumption. Therefore, this work may provide a new perspective for the green preparation of dissolving pulp that can be used to produce lyocell fiber after ash and metal ion treatment.