Adsorptive removal of benzene and toluene from aqueous solutions by oxygen-functionalized multi-walled carbon...

One of the current directions for sustainable development is to use waste resources to create materials that reduce environmental pollution. In this study, multi-walled carbon nanotubes (MWCNT) and their oxygen-functionalized forms (HNO₃/H₂SO₄-oxidized MWCNT, NaOCl-oxidized MWCNT, and H₂O₂-oxidized MWCNT) were first synthesized from activated carbon (AC) derived from rice husk waste. A comprehensive comparison of the morphological and structural properties of these materials was conducted using FT-IR, BET, XRD, SEM, TEM, TGA, Raman spectroscopy, and surface charge analysis. The morphology study suggests that the synthesized MWCNTs have an average outer and inner diameter of about 40 and 20 nm, respectively. Additionally, the NaOCl-oxidized MWCNT possesses the largest interspaces between nanotubes, while the HNO₃/H₂SO₄-oxidized CNT has the most oxygen-functional groups, including -COOH, (Ar)-OH, and C-OH. The adsorption capacities of these materials were also compared for the removal of benzene and toluene. Experimental results have shown that while porosity is the primary factor governing the benzene and toluene adsorption onto AC, functionalization degree and surface chemical characteristics are the determining factors in the adsorption capacity of the as-prepared MWCNTs. The adsorption capacity of these aromatic compounds in an aqueous solution increases in the following order: AC < MWCNT < HNO₃/H₂SO₄-oxidized MWCNT < H₂O₂-oxidized MWCNT < NaOCl-oxidized MWCNT, and in all cases, toluene is more readily adsorbed than benzene under similar adsorption conditions. Wherein the uptake of both pollutants by the prepared adsorbents in this study is best described by the Langmuir isotherm and obeys the pseudo-second-order kinetic model. The adsorption mechanism was discussed in a detailed manner.