Environmental factors strongly influence the leaching of di(2-ethylhexyl) phthalate from polyvinyl chloride...

Phthalic acid esters (phthalates) are an important group of additives (plasticizers) to ensure the flexibility and stability especially of polyvinyl chloride (PVC) and to enable its processing. However, phthalates like di(2-ethylhexyl) phthalate (DEHP) are harmful for aquatic organisms due to their endocrine disrupting effects and toxicity. For the assessment of exposure concentrations, thorough understanding of leaching kinetics of phthalates from PVC (micro-) plastics into aqueous environments is necessary. This study investigates how environmental factors influence the leaching of phthalates from PVC microplastics into aquatic systems. The leaching of phthalates from PVC microplastics into aqueous media is limited by aqueous boundary layer diffusion (ABLD) and thus, process-specific parameters can be affected by environmental factors such as salinity and the flow conditions. We conducted batch leaching experiments to assess the influence of salinity and flow conditions (turbulence) on the leaching of DEHP from PVC microplastics into aqueous media. DEHP is salted out with increasing salinity of the solution and a salting-out coefficient for DEHP of 0.46 was determined. The partitioning coefficient of DEHP between PVC and water K_PVC/W increased with increasing salinity from 10^8.52 L kg^-1 in a 1 mM KCl solution to 10^8.75 L kg^-1 in artificial seawater thereby slowing down leaching. Increasing flow velocities led to higher leaching rates because the ABL thickness decreased from 1315 µm at 0 rpm shaking speed (no-flow conditions) to 38.4 µm at 125 rpm (turbulent conditions). Compared to salinity, turbulence had a more pronounced effect on leaching. Increasing the flow velocity led to a 35-fold decrease in the leaching rate, while increasing salinity led to a 2-fold increase. By calculating specific leaching times, that is, leaching half-lives (t_1/2), time frames for leaching in different aquatic systems such as rivers and the ocean were determined. Given ABLD-limited leaching, DEHP is leached faster from PVC microplastics in rivers (t_1/2 > 49 years) than in the ocean (t_1/2 > 398 years). In both systems, PVC microplastics are a long-term source of phthalates.