Push-out Bond Strength of Fiber Posts in Long-Term Hypobaric Pressure Changes

BACKGROUND: The purpose of this study was to evaluate the bond strength of fiber posts with different mixing methods and insertion into root canal techniques in long-term hypobaric pressure changes.METHODS: We chose and decoronated 42 teeth with straight and single root canals. After post-space preparation, the posts were cemented with hand-mixed and auto-mixed resin cements that were inserted into the canals with an endodontic file (lentilo), dual-barrel syringe, and root canal tip (14 for each group). After cementation, each group was divided into two subgroups (N = 7): the control (ambient pressure) group and the hypobaric pressure group. The samples were exposed to hypobaric pressure 90 times. They were cut into 2-mm-thick segments and the push-out bond strength test was performed using a Universal Testing Machine. One-way ANOVA tests, Bonferroni tests, and Student-t-tests were used for statistical analysis.RESULTS: The environmental pressure changes and insertion techniques affected the bond strength values. The auto-mixed with root-canal tip group showed the highest push-out bond strength values in both hypobaric (dual-barrel syringe group: 10.01 MPa; root-canal tip group: 11.61 MPa) and control (dual-barrel syringe group: 12.29 MPa; root-canal tip group: 14.58 MPa) group. In all root segments, the bond strength values of hypobaric groups were lower than atmospheric pressure groups. The most frequent failure type was adhesive between dentin and cement in all groups.DISCUSSION: Dentists should use auto-mixed self-adhesive resin with a root canal tip for post cementations in patients likely to be exposed to hypobaric pressure changes.Ozkan Ata S, Ata N, Yazgan E, Akkor T. Ugurlutan R.