Fabrication of transparent cellulose nanofibril composite film with smooth surface and ultraviolet blocking ability...

Ecofriendly multifunctional films with only biomass-based components have gathered significant interest from researchers as next-generation materials. Following this trend, a TEMPO-oxidized cellulose nanofibril (TOCNF) film containing hydrophilic lignin (CL) was fabricated. To produce the lignin, peracetic acid oxidation was carried out, leading to the introduction of carboxyl groups into the lignin structure. By adding hydrophilic lignin, various characteristics (e.g., surface smoothness, UV protection, antimicrobial activity, and barrier properties) of the TOCNF film were enhanced. In particular, the shrinkage of CNF was successfully prevented by the addition of CL, which is attributed to the lower surface roughness (R_a) from 18.93 nm to 4.99 nm. As a result, the smooth surface of the TOCNF/CL film was shown compared to neat TOCNF film and TOCNF/Kraft lignin composite film. In addition, the TOCNF/CL film showed a superior UV blocking ability of 99.9 % with high transparency of 78.4 %, which is higher than that of CNF-lignin composite films in other research. Also, water vapor transmission rate was reduced after adding CL to TOCNF film. Consequently, the developed TOCNF/CL film can be potentially utilized in various applications, such as food packaging.