Effect of toothpaste tablets on gloss and surface roughness of resin-based composite materials

To evaluate the effects of toothpaste tablets on the gloss and surface roughness of resin-based composite materials and determine the relationship between gloss and roughness.

Rectangular jigs were designed and printed. Wells (2 mm deep x 7 mm diameter) were filled with Filtek Supreme Ultra A2B, light-cured and polished. A small-area glossmeter was used for gloss (GU) measurements and a profilometer for roughness measurements (Ra) at baseline and after challenge with each toothpaste. An automated tooth-brushing machine was set at 120 strokes/minute for a total of 10,000 strokes to evaluate four test groups with 16 specimens in each group. NC: Brushing with distilled water; TABS: Colgate Anywhere Travel Tooth Tabs; CP: Colgate Cavity Protection Toothpaste and AW: Colgate Whitening Advanced Toothpaste. Kruskal-Wallis test was used to test the difference in gloss and surface roughness among the groups and Pearson correlation was used to compare the relationship between gloss and roughness.

There was no statistically significant difference in gloss and roughness among the four groups at baseline. At post-brushing, there was a statistically significant difference among the groups (P< 0.001) with increased roughness and decreased gloss for CP and AW when compared to TABS. There was a statistically significant correlation between post-brushing roughness and post-brushing gloss (P< 0.001, rho: -0.815). Thus, the higher the surface roughness the lower the gloss.

Toothpaste tablets retain better gloss and roughness of resin-based composite materials when compared to conventional toothpastes.