Strong interlayer coupling in p-Te/n-CdSe van der Waals heterojunction for self-powered photodetectors with fast...

Self-driven photodetectors, which can detect optical signals without external voltage bias, are highly attractive in the field of low-power wearable electronics and internet of things. However, currently reported self-driven photodetectors based on van der Waals heterojunctions (vdWHs) are generally limited by low responsivity due to poor light absorption and insufficient photogain. Here, we report p-Te/n-CdSe vdWHs utilizing non-layered CdSe nanobelts as efficient light absorption layer and high mobility Te as ultrafast hole transporting layer. Benefiting from strong interlayer coupling, the Te/CdSe vdWHs exhibit stable and excellent self-powered characteristics, including ultrahigh responsivity of 0.94 A W^-1, remarkable detectivity of 8.36 × 10¹² Jones at optical power density of 1.18 mW cm^-2 under illumination of 405 nm laser, fast response speed of 24 µs, large light on/off ratio exceeding 10⁵, as well as broadband photoresponse (405-1064 nm), which surpass most of the reported vdWHs photodetectors. In addition, the devices display superior photovoltaic characteristics under 532 nm illumination, such as large V_oc of 0.55 V, and ultrahigh I_sc of 2.73 µA. These results demonstrate the construction of 2D/non-layered semiconductor vdWHs with strong interlayer coupling is a promising strategy for high-performance and low-power consumption devices.