Interfacial Electronic Interaction in In₂O₃/Poly(3,4-ethylenedioxythiophene)-Modified Carbon Heterostructures for...

Formate, as an important chemical raw material, is considered to be one of the most promising products for industrialization among CO₂ electroreduction reaction (CO₂RR) products, but it still suffers from poor selectivity and a low formation rate at a high current density on account of the competitory hydrogen evolution reaction. Herein, the heterogeneous nanostructure was constructed by anchoring In₂O₃ nanoparticles on poly(3,4-ethylenedioxythiophene) (PEDOT)-modified carbon black (In₂O₃/PC), in which the PEDOT polymer interface layer could immobilize In₂O₃ nanoparticles and obtain a notable reduction in electron transfer resistance among the In₂O₃ particles, showing a 27% increase in the total electron transfer rate. The optimized In₂O₃/PC with rich heterogeneous interfaces selectively reduced CO₂ to formate with a high FE of 95.4% and a current density of 251.4 mA cm^-2 under -1.18 V vs RHE. Also, the formate production rate for In₂O₃/PC was up to 7025.1 μmol h^-1 cm^-2, surpassing most previously reported CO₂RR catalysts. The in situ XRD results revealed that In₂O₃ particles were reduced to metallic indium (In) as catalytic active sites during CO₂RR. DFT calculations verified that a strong interface interaction between In sites and PC induced electron transfer from In sites to PC, which could optimize the charge distribution of active sites, accelerate electron transfer, and elevate the p-band center of In sites toward the Fermi level, thereby lowering the adsorption energy of *OCHO intermediates for CO₂ conversion to formate.