Branched Aluminum Nanocrystals with Internal Hot Spots: Synthesis and Single-Particle Surface-Enhanced Raman
Fei Peng1, Shao-Yong Lu1, Pan-Qi Sun1
1State Key Laboratory of Supramolecular Structure and Materials, College of Chemistry, Jilin University, Changchun 130012, China.
Abstract:
Owing to their unique and sustainable surface plasmonic properties, Al nanocrystals have attracted increasing attention for plasmonic-enhanced applications, including single-particle surface-enhanced Raman scattering (SERS). However, whether Al nanocrystals can achieve single-particle SERS is still unknown, mainly due to the synthetic difficulty of Al nanocrystals with internal gaps. Herein, we report a regrowth method for the synthesis of Al nanohexapods with tunable and uniform internal gaps for single-particle SERS with an enhancement factor of up to 1.79 × 108. The uniform branches of the Al nanohexapods can be systematically tuned regarding their dimensions, terminated facets, and internal gaps. The Al nanohexapods generate hot spots concentrated in the internal gaps due to the strong plasmonic coupling between the branches. A single-particle SERS measurement of Al nanohexapods shows strong Raman signals with maximum enhancement factors comparable to that of Au counterparts. The large enhancement factor indicates that Al nanohexapods are good candidates for single-particle SERS.