Near-ultraviolet irradiation to stimulate unmodified polyether ether ketone to achieve stable and sustainable...

This study aims to investigate the cytotoxicity and sustainable antibacterial activity of unmodified PEEK under specific wavelength light treatment (365 nm), and its antibacterial mechanism was also preliminarily discussed.

A near-ultraviolet source with a wavelength of 365 nm and a power of 5 W were selected. The irradiation time was 30 min, and the distance was 100 mm. A water contact angle tester was used to characterize the surface of the PEEK after 1-15 light treatments. MC3TC-E1 cells were used to evaluate the cytotoxicity of the materials under light treatment. Five kinds of common oral bacteria were detected in vitro, and antibacterial efficiency was determined by colony-forming unit (CFU) and scanning electron microscope (SEM). The antibacterial mechanism of PEEK under light was preliminarily discussed by spectrophotometry. The membrane rupture of Staphylococcus aureus and Escherichia coli was detected by lactate dehydrogenase. Staphylococcus aureus and Staphylococcus mutans were selected for the cyclic antibacterial test. Statistical analysis was performed by one-way analysis of variance and Tukey multiple range test. A significance level of 0.05 was considered (α = 0.05).

The results of the cell experiment showed that PEEK had no cytotoxicity (P > 0.05). CFU results showed that PEEK had an obvious antibacterial effect on Staphylococcus aureus, Staphylococcus mutans, Staphylococcus gordonii and Staphylococcus sanguis, but had no antibacterial effect on Escherichia coli (P < 0.05). The SEM results also verified the above antibacterial effect. The existence of singlet oxygen was confirmed by spectrophotometry. Meanwhile, the rupture of Staphylococcus aureus membrane was verified by lactate dehydrogenase assay. The water contact angle of the PEEK surface did not change significantly after 15 cycles of light treatment. Cyclic antibacterial experiments showed that the antibacterial effect was sustainable.

This study showed that PEEK has good cytocompatibility with stable and sustainable antibacterial properties under near-ultraviolet. It provides a new idea to solve the non-antibacterial property of PEEK, and also provides a theoretical basis for its further application in dentistry.