Microstructural and Mechanical Characterization of Colloidal Processed WC/(W5Vol%Ni) via Spark Plasma Sintering

This study investigates the sintering behaviour and properties of WC-based composites in which WC was mixed with W5vol%Ni in concentrations of 10vol% and 20vol%. Colloidal processing in water and spark plasma sintering were employed to disperse the WC particles and facilitate sintering. The addition of W5vol%Ni improved the sintering process, as evident from a lower onset temperature of shrinkage determined through dilatometric studies. All samples exhibited the formation of tungsten monocarbide (W₂C), with a more pronounced presence in the WC/20(W5vol%Ni) composite. Sintering reached its maximum rate at 1550 °C and was completed at 1600 °C, resulting in a final density exceeding 99.8%. X-ray diffraction analysis confirmed the detection of WC and W₂C phases after sintering. The observed WC content was higher than expected, which may be attributed to carbon diffusion during the process. Macro-scale mechanical characterisations revealed that the WC/10(W5vol%Ni) composite exhibited a hardness of 18.9 GPa, while the WC/20(W5vol%Ni) composite demonstrated a hardness of 18.3 GPa. Increasing the W5vol%Ni binder content caused a decrease in mechanical properties due to the formation of W₂C phases. This study provides valuable insights into the sintering behavior and properties of WC/W5vol%Ni composites, offering potential applications in extreme environments.