Microstructure Evolution of the Near-Surface Deformed Layer and Corrosion Behavior of Hot Rolled AA7050 Aluminum...

The current study investigates the influence of hot rolling on the microstructure evolution of the near-surface region on AA7050 aluminum alloy and the corrosion performance of the alloy. It is revealed that hot rolling resulted in grain refinement in the near-surface region, caused by dynamic recrystallization, and equiaxed grains less than 500 nm can be clearly observed. Fibrous grains were evident in the hot rolled AA7050 aluminum alloy with relatively lower rolling temperature or larger rolling reduction, caused by the more severe elemental segregation at grain boundaries, which inhibited the progression of dynamic recrystallization. The density of the precipitates in the fibrous grain layer was higher, compared with those in the equiaxed grain layer, due to the increased dislocation density, combined with more severe elemental segregation, which significantly promoted the nucleation of precipitates. With the co-influence exerted by low density of precipitates and dislocations on the improvement of the corrosion performance of the alloy, the rolled AA7050 alloy with decreased density of precipitates and dislocations exhibited better corrosion resistance.