Properties of Red Mud Neutralized with Sulfuric Acid and Effects on Cement Mortar

The purpose of this study was to recycle red mud, an industrial byproduct that generates 300,000 tons per year, into the construction industry. Red mud was prepared as a liquid, neutralized with sulfuric acid, and replaced with cement mortar. The properties of liquefied red mud (LRM) neutralized with sulfuric acid (LRM + S) were investigated as well as its effect on cement mortar's mechanical and hydration characteristics. The pH of LRM + S stabilized at 7.6; its SO₃ content was ~4.19% higher than that of LRM. Sulfites were contributed by calcium and sodium sulfate. The flows and setting times of the mortars containing LRM and LRM + S decreased as the substitution rate increased. The compressive strength of mortar that replaced 5% of cement with LRM + S was similar to that of the plain cement mortar. Scanning electron microscopy and X-ray diffraction revealed that the hydration products of LRM + S-containing cement mortar were similar to those of the plain cement mortar. Thus, LRM + S can be used as a cement substitute.