Human nasal cartilage: Functional properties and structure-function relationships for the development of tissue...

Nose reconstruction often requires scarce cartilage grafts. Nasal cartilage properties must be determined to serve as design criteria for engineering grafts. Thus, mechanical and biochemical properties were obtained in multiple locations of human nasal septum, upper lateral cartilage (ULC), and lower lateral cartilage (LLC). Within each region, no statistical differences among locations were detected, but anisotropy at some septum locations was noted. In the LLC, the tensile modulus and ultimate tensile strength (UTS) in the inferior-superior direction were statistically greater than in the anterior-posterior direction. Cartilage from all regions exhibited hyperelasticity in tension, but regions varied in degree of hyalinicity (i.e., Col II:Col I ratio). The septum contained the most collagen II and least collagen I and III, making it more hyaline than the ULC and LLC. The septum had a greater aggregate modulus, UTS, and lower total collagen/wet weight (Col/WW) than the ULC and LLC. The ULC had greater tensile modulus, DNA/WW, and lower glycosaminoglycan/WW than the septum and LLC. The ULC had a greater pyridinoline/Col than the septum. Histological staining suggested the presence of chondrons in all regions. In the ULC and LLC, tensile modulus correlated with total collagen content, while aggregate modulus correlated with pyridinoline content and weakly with pentosidine content. However, future studies should be performed to validate these proposed structure-function relationships. This study of human nasal cartilage provides 1) crucial design criteria for nasal cartilage tissue engineering efforts, 2) quantification of major and minor collagen subtypes and crosslinks, and 3) structure-function relationships. Surprisingly, the large mechanical properties found, particularly in the septum, suggests that nasal cartilage may experience higher-than-expected mechanical loads. STATEMENT OF SIGNIFICANCE: While tissue engineering holds promise to generate much-needed cartilage grafts for nasal reconstruction, little is known about nasal cartilage from an engineering perspective. In this study, the mechanical and biochemical properties of the septum, upper lateral cartilage (ULC), and lower lateral cartilage (LLC) were evaluated using cartilage-specific methods. For the first time in this tissue, all major and minor collagens and collagen crosslinks were measured, demonstrating that the septum was more hyaline than the ULC and LLC. Additionally, new structure-function relationships in the ULC and LLC were identified. This study greatly expands upon the quantitative understanding of human nasal cartilage and provides crucial engineering design criteria for much-needed nasal cartilage tissue engineering efforts.