Electrospinning of Biodegradable, Monolithic Membrane with Distinct Bimodal Micron-Sized Fibers and Nanofibers for
Jian Chen1, Boyang Yu2, Jian Zhu1
1Department of Materials Science and Engyneering, Southern University of Science and Technology, 1088 Xueyuan Road, Nanshan District, Shenzhen City, Guangdong Province 518000, China.
Abstract:
Atmospheric particulate matter (PMs) pollution has raised increasing public concerns, especially with the outbreak of COVID-19. The preparation of high-performance membranes for air filtration is of great significance. Herein, the biosynthetic polymer poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) was adopted to create a hierarchical structure and biodegradable nonwoven membrane for PMs filtration through a facile directly electrospinning method. The as-prepared membranes with hierarchical structure contain abundant nanowires (5-100 nm) and microfibers (2-5 μm) with different diameter (1000-5000 nm). We have achieved realization of formation mechanisms of such bimodal micro- and nanofibers, which stem from the branching of microfiber at early stage of electrospinning. The PHBV membranes exhibit a very high PM0.3 removal efficiency of 99.999% and PM2.5 removal efficiency of 100% with 0.077% standard atmospheric pressure in the air flow speed of 5.3 cm/s. More importantly, the PHBV membranes can be completely disintegrated within 1 week under composted conditions, indicating the great biodegradability of PHBV membranes. Our work provides insights for the development of biodegradable, high performance air filters for pollutants, molds, bacteria, and viruses.