Crystalline AuNP-Decorated Strontium Niobate Thin Films: Strain-Controlled AuNP Morphologies and Optical Properties...

Gold nanoparticle (AuNP) decoration is a commonly used method to enhance the optical responses in many applications such as photocatalysis, biosensing, solar cells, etc. The morphology and structure of AuNPs are essential factors determining the functionality of the sample. However, tailoring the growth mechanism of AuNPs on an identical surface is not straightforward. In this study, AuNPs were deposited on the surface of a perovskite thin film, strontium niobate (SNO), using pulsed laser deposition (PLD). AuNPs exhibited a dramatic variation in their growth mechanisms, depending on whether they were deposited on SNO thin films grown on magnesium oxide (SNO/MgO) or strontium titanate (SNO/STO) substrates. On SNO/MgO, the Au aggregates form large NPs with an average size of up to 3500 nm². These AuNPs are triangular with sharp edges and corners. The out-of-plane direction of growth is favored, and the surface coverage ratio by AuNPs is low. When deposited on SNO/STO, the average size of AuNPs is much smaller, i.e., ∼250 nm². This reduction in the average size is accompanied by an increase in the number density of NPs. AuNPs on SNO/STO have a round shape and high coverage ratio. Such an impact from the substrate selection on the AuNP structure is significant when the sandwiched SNO film is below 80 nm thickness and is weakened for 200 nm of SNO films. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to characterize all samples. Strain analysis was used to explain the growth mechanism of AuNPs. The average height of AuNPs was measured by using atomic force microscopy (AFM). Ellipsometry in the visible-near-infrared (vis-NIR) region was used to characterize the optical response of all samples. AuNP-decorated SNO/MgO and SNO/STO thin films exhibit different optical properties, with only gold-decorated SNO/MgO samples showing a size-dependent epsilon-near-zero behavior of nanoparticles. These results provide an additional route to control the structure of AuNPs. They can be used for various plasmonic applications like the design and development of strain-engineered gold-nanoparticle-decorated devices for surface-enhanced Raman spectroscopy (SERS) and photocatalysis.