Fabrication of polyethyleneimine functionalized magnetite nanoparticles for recyclable recovery of fucoidan from...

Fucoidan is a kind of natural water-soluble fucose-rich sulfated polysaccharide with promising applications in the food and pharmaceutical industry. However, the traditional methods for fucoidan recovery from aqueous solution are expensive, time-consuming, and environmentally unfriendly. In this work, polyethyleneimine functionalized magnetite nanoparticles (PEI-MNPs) with well-defined core-shell structures were prepared by a Layer-by-Layer (LbL) approach using sodium tripolyphosphate (STPP) as a cross-linker. The as-prepared PEI-MNPs showed improved adsorption capability towards fucoidan at pH 4-8 due to the high density of cationic groups on the surfaces and the absence of internal pores. It was found that the adsorption process of fucoidan onto PEI-MNPs can reach to equilibrium in 50 min at room temperature. The maximum q_e derived from the Langmuir isotherm at room temperature was 169.1 mg per g at a pH of 7. A selective fucoidan capture over a model protein BSA can be realized by adjusting pH (6-8) and salt concentration (0.5-2.5 M). The PEI-MNPs loading with fucoidan can be isolated from the final products by a neodymium magnet and regenerated by 4 M NaCl solution as stripping reagent. Therefore, this novel kind of PEI-MNP could be a promising candidate for highly efficient and recyclable recovery of fucoidan from an aqueous solution.