Highly selective photocatalytic CO₂ reduction and hydrogen evolution facilitated by oxidation induced nitrogen...

The introduction of nitrogen vacancies into polymeric carbon nitride (PCN) has been attested to be a reliable strategy to enhance photocatalytic performance. Nitrogen vacancies were considered as active sites to promote the adsorption of target molecules and capture photoexcited electrons to inhibit the recombination of charge pairs, accelerate photoinduced electrons to participate in photocatalytic reaction. In this paper, a series of PCN with rich nitrogen vacancies were prepared by etching of chromic acid solution. Sample 20KCSCN had the highest photocatalytic performance whose evolution efficiency of CO₂ to CO and CH₄ can reach 3.9 and 0.5 μmol·g^-1·h^-1, respectively. These evolution efficiencies are 2.9 and 4 times higher than that of the PCN. Meanwhile, 20KCSCN demonstrates high CO conversion selectivity and stability. The successful introduction of nitrogen vacancies not only increases the active sites of PCN surface, but also optimizes the optical structure, which dramatically boosts the separation of photoexcited charge pairs and the reduction capacity of photogenerated electrons. The enhancement mechanism for photocatalytic CO₂ reduction performance of PCN was proposed. Besides, photocatalytic H₂ evolution experiments were performed on all samples to confirm the universality of PCN photocatalytic activity enhancement etched by chromic acid solution. H₂ evolution rate on 20KCSCN can reach 652 μmol·g^-1·h^-1, which is 1.6-fold higher than that on PCN (254 μmol·g^-1·h^-1) after 4 h irradiation under a 300 W Xe lamp. This work offers new venue for introducing nitrogen vacancies in PCN to regulate photoexcited charge pairs transfer. The photocatalytic enhancement of CO₂ reduction could be used to alleviate the serious issue of excessive CO₂ emission and energy crisis.