Interface Characteristics of Tungsten-Particle-Reinforced Zr-Based Bulk-Metallic-Glass Composites with Different
Haoyu Jin1, Huie Hu1, Junhan Chi1
1Department of Chemistry and Materials, Naval University of Engineering, Wuhan 430033, China.
Abstract:
This study investigated the interfacial characteristics of tungsten-particle-reinforced Zr-based bulk-metallic-glass composites (Wp/Zr-BMGs) with varying tungsten-particle sizes. To this end, Wp/Zr-BMGs with three different Wp sizes were fabricated using spark plasma sintering. Subsequently, the microstructures and interfacial structures of the Wp/Zr-BMGs were extensively examined, and the mechanical properties of the microzone at the Wp/Zr-BMG interface were evaluated using a nanoindentation method. The results revealed that the interfaces of Wp/Zr-BMGs, irrespective of the Wp size, exhibited dissolution-diffusion characteristics. Moreover, the thickness of the interface diffusion layer was positively correlated to the size of Wp. The addition of Wp enhanced the elastic modulus and hardness of Zr-BMGs at the interface, as these effects are inversely related to the Wp size. Furthermore, this study established a relationship between the interfacial mechanical properties and the interfacial characteristics of particle-reinforced bulk-metallic-glass composites. Thus, this study can serve as a guide for future research in the field of Wp/Zr-BMGs and similar particle-reinforced composites.