Hydrothermal Synthesis of a Technical Lignin-Based Nanotube for the Efficient and Selective Removal of Cr(VI) from...

Aminated lignin (AL) was obtained by modifying technical lignin (TL) with the Mannich reaction, and aminated lignin-based titanate nanotubes (AL-TiNTs) were successfully prepared based on the AL by a facile hydrothermal synthesis method. The characterization of AL-TiNTs showed that a Ti-O bond was introduced into the AL, and the layered and nanotubular structure was formed in the fabrication of the nanotubes. Results showed that the specific surface area increased significantly from 5.9 m²/g (TL) to 188.51 m²/g (AL-TiNTs), indicating the successful modification of TL. The AL-TiNTs quickly adsorbed 86.22% of Cr(VI) in 10 min, with 99.80% removal efficiency after equilibration. Under visible light, AL-TiNTs adsorbed and reduced Cr(VI) in one step, the Cr(III) production rate was 29.76%, and the amount of total chromium (Cr) removal by AL-TiNTs was 90.0 mg/g. AL-TiNTs showed excellent adsorption capacities of Zn²⁺ (63.78 mg/g), Cd²⁺ (59.20 mg/g), and Cu²⁺ (66.35 mg/g). After four cycles, the adsorption capacity of AL-TiNTs still exceeded 40 mg/g. AL-TiNTs showed a high Cr(VI) removal efficiency of 95.86% in simulated wastewater, suggesting a promising practical application in heavy metal removal from wastewater.