Structural and Optical Characterizations of Polymethyl Methacrylate Films with the Incorporation of Ultrafine...

The structural and optical characterizations of nanocomposite films of polymethyl methacrylate (PMMA) and SiO₂/TiO₂ composites prepared via the spin-coating technique were investigated using different SiO₂:TiO₂ ratios. The SiO₂/TiO₂ nanocomposites were synthesized using the sonochemical process with Si:Ti precursor ratios of 1:0.1, 1:0.5, 1:1, 1:2, 1:4, and 0:1. All characterizations of ultrafine SiO₂/TiO₂ particles were loaded at 1 wt.% in a PMMA matrix for the fabrication of transparent SiO₂/TiO₂/PMMA composite films. The phase structure and morphology of SiO₂/TiO₂/PMMA composite films were monitored using X-ray diffraction, optical microscopy, and field-emission scanning electron microscopy. A surface roughness analysis of SiO₂/TiO₂/PMMA nanocomposite films was conducted using atomic force microscopy. For optical characterization, transmission properties with different incident angles of SiO₂/TiO₂/PMMA composite films were analyzed with UV-vis spectrophotometry. The water contact angles of SiO₂/TiO₂/PMMA composite films were analyzed to identify hydrophilic properties on film surfaces. Photocatalytic reactions in SiO₂TiO₂ composite films under UV irradiation were evaluated using rhodamine B dye degradation. The optimal condition of SiO₂/TiO₂/PMMA nanocomposite films was obtained at a 1:1 SiO₂:TiO₂ ratio in self-cleaning applications, resulting from good particle dispersion and the presence of the TiO₂ phase in the composite.