Effects of various functional monomers' reaction on the surface characteristics and bonding performance of
Huei-Yu Huang1,2, Sheng-Wei Feng2, Kuan-Yu Chiang3
1Department of Dentistry, Taipei Medical University Shuang Ho Hospital, New Taipei City, Taiwan.
Purpose:
Polyetheretherketone (PEEK) is a new polymeric material that has received significant attention in dentistry because of its mechanical properties, biocompatibility, and aesthetics. However, the bonding performance of PEEK to other materials is not preferable. This study aimed to analyze the variations in the surface characteristics of PEEK under the chemical action of primers containing different functional monomers or polymers and to evaluate the bonding performance of PEEK and dental cement.
Methods:
Disk-shaped PEEK samples were prepared by dental milling, blasting with alumina oxide, and covering with primers containing functional monomers or polymers. The surface characteristics of the samples were analyzed by microscopy and spectroscopy. The shear bond strength (SBS) between PEEK and dental cement, with and without thermocycling, was tested using a universal testing machine. Finally, the data were statistically analyzed and compared.
Results:
Functional monomers or polymers were successfully bonded to the surface of PEEK. This treatment significantly improved its hydrophilicity and surface free energy (P < 0.05). The primer containing pentaerythritol triacrylate had the highest SBS without thermocycling (13.89 MPa). Meanwhile, the primers containing urethane dimethacrylate (UDMA) and methyl methacrylate (MMA) (abbreviated as the HC group) showed the highest SBS and lowest reduction (25.51%) after thermocycling. Notably, all the testing groups achieved the ISO10477 standard of 5 MPa. After thermocycling, adhesive failure accounted for the largest proportion of failures in all the groups except the HC group.
Conclusions:
The chemical priming treatment can significantly improve the SBS of PEEK and dental cement. Moreover, a primer containing both UDMA and MMA can provide improved bonding for PEEK materials.
Related Concept Videos
01:14Polymer Classification: Architecture
02:36Crown Ethers
01:20Types of Step-Growth Polymers: Polyesters
Polyesters are commonly prepared from terephthalic acid and ethylene glycol; the crude product is known as poly(ethylene terephthalate) or PET. However, polyesters are synthesized industrially by transesterification of dimethyl terephthalate with ethylene glycol at 150 °C. The two reactants and the...
01:24Characteristics and Nomenclature of Copolymers
01:00Characteristics and Nomenclature of Homopolymers
02:17Physical Properties of Ethers
An ether molecule has a net dipole moment due to the polarity of C–O bonds. Subsequently, boiling points of ethers are lower than those of alcohols of comparable molecular weight and slightly higher than those of hydrocarbons of comparable molecular weight (Table 1).
Ethers can act as hydrogen bond acceptors, making them more water-soluble than hydrocarbons, but since ethers cannot act as hydrogen bond donors, they are much less soluble in water than alcohols. Ethers are considered...