Growth kinetics and substrate stability during high-temperature molecular beam epitaxy of AlN nanowires

We study the molecular beam epitaxy of AlN nanowires between 950 °C and 1215 °C, well above the usual growth temperatures, to identify optimal growth conditions. The nanowires are grown by self-assembly on TiN(111) films sputtered onto Al₂O₃. Above 1100 °C, the TiN film is seen to undergo grain growth and its surface exhibits {111} facets where AlN nucleation preferentially occurs. Modeling of the nanowire elongation rate measured at different temperatures shows that the Al adatom diffusion length maximizes at 1150 °C, which appears to be the optimum growth temperature. However, analysis of the nanowire luminescence shows a steep increase in the deep-level signal already above 1050 °C, associated with O incorporation from the Al₂O₃substrate. Comparison with AlN nanowires grown on Si, MgO and SiC substrates suggests that heavy doping of Si and O by interdiffusion from the TiN/substrate interface increases the nanowire internal quantum efficiency, presumably due to the formation of a SiNor AlOpassivation shell. The outdiffusion of Si and O would also cause the formation of the inversion domains observed in the nanowires. It follows that for optoelectronic and piezoelectric applications, optimal AlN nanowire ensembles should be prepared at 1150 °C on TiN/SiC substrates and will require anex situsurface passivation.