Ocimum sanctum Leaf Extract-Assisted Green Synthesis of Pd-Doped CuO Nanoparticles for Highly Sensitive and Selective
Anit K Ambedkar1, Durvesh Gautam1, Sagar Vikal1
1Smart Materials and Sensor Laboratory, Department of Physics, Chaudhary Charan Singh University, Meerut, Uttar Pradesh 250004, India.
Abstract:
In view of facile, cost-effective, and environmentally friendly synthetic methods, palladium-doped copper oxide (Pd-CuO) nanoparticles have been synthesized from Ocimum sanctum (commonly known as "Tulsi") phytoextract for gas-sensing applications. The structural, morphological, and compositional properties of Pd-doped CuO nanoparticles were studied using various techniques such as XRD, FESEM, XPS, and EDX. The characterization results confirmed the doping of Pd on CuO nanoparticles, and Pd-CuO nanostructures appear as nanoflakes in FESEM analysis. The gas-sensing response of Pd (1.12 wt %)-CuO nanoflake-based sensor was measured at 5-100 ppm concentration of different gases, NO2, H2S, NH3, and H2, at 125 °C. Gas-sensing tests reveal that the sensitivity of the sensor were 81.7 and 38.9% for 100 and 5 ppm concentrations of NO2, respectively, which was significantly greater than that of pure CuO. The response and recovery times of the sensor were 72 and 98 s for 100 ppm of NO2 gas, while they were 90 and 50 s for 5 ppm NO2. The calculated limit of detection (LOD) value of the sensor is 0.8235. This appealing LOD is suitable for real-time gas detection. The gas sensor was found to exhibit excellent selectivity toward NO2 gas and repeatability and stability in humid (80%) conditions. The Pd doping in CuO nanostructures plays a significant role in escalating the sensitivity and selectivity of CuO-based NO2 gas sensor suitable to work at low operating temperatures.