Reexamining the Role of Solution-Cast Ferroelectric Polymer Interlayer toward Enhanced Efficiency and Stability in
Wei Sun1, Yiwei Fu1, Lianmeng Cui1
1School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China.
Abstract:
Interfacial modification is crucial for achieving efficient and stable organic solar cells (OSCs). Herein, an N,N-dimethylformamide (DMF) solution-cast poly(vinylidene fluoride-co-trifluoroethylene) (P(VDF-TrFE)) interlayer was applied to enhance the efficiency and stability of a range of OSCs, and the underlying mechanism was revealed via morphological and device physics studies. DMF rinse during the P(VDF-TrFE) interlayer casting process strengthens π-π stacking of the active layer with fibril aggregation, optimized phase separation, and vertical component distribution, while the P(VDF-TrFE) interlayer with rich diploes contributes to increased surface potential and internal electric field. The synergistic effect of the P(VDF-TrFE) interlayer and DMF rinse increases the PCEs of PM6:IT-4F, PM6:C5-16, and PM6:L8-BO OSCs from 12.7, 17.9, and 18.2% to 13.1, 18.7, and 18.8%, respectively. Additionally, OSCs containing the P(VDF-TrFE) interlayer also showed improved storage stability.
More Related Videos
06:49In situ Grazing Incidence Small Angle X-ray Scattering on Roll-To-Roll Coating of Organic Solar Cells with Laboratory X-ray Instrumentation
Published on: March 2, 2021
11:38Influence of Hybrid Perovskite Fabrication Methods on Film Formation, Electronic Structure, and Solar Cell Performance
Published on: February 27, 2017