Enhanced Thermoelectric Properties of Nb-Doped Ti(FeCoNi)Sb Pseudo-Ternary Half-Heusler Alloys Prepared Using the...

Pseudo-ternary half-Heusler thermoelectric materials, which are formed by filling the B sites of traditional ternary half-Heusler thermoelectric materials of ABX with equal atomic proportions of various elements, have attracted more and more attention due to their lower intrinsic lattice thermal conductivity. High-purity and relatively dense Ti_1-Nb(FeCoNi)Sb (x = 0, 0.01, 0.03, 0.05, 0.07 and 0.1) alloys were prepared via microwave synthesis combined with rapid hot-pressing sintering, and their thermoelectric properties are investigated in this work. The Seebeck coefficient was markedly increased via Nb substitution at Ti sites, which resulted in the optimized power factor of 1.45 μWcm^-1K^-2 for n-type Ti_0.93Nb_0.07(FeCoNi)Sb at 750 K. In addition, the lattice thermal conductivity was largely decreased due to the increase in phonon scattering caused by point defects, mass fluctuation and strain fluctuation introduced by Nb-doping. At 750 K, the lattice thermal conductivity of Ti_0.97Nb_0.03(FeCoNi)Sb is 2.37 Wm^-1K^-1, which is 55% and 23% lower than that of TiCoSb and Ti(FeCoNi)Sb, respectively. Compared with TiCoSb, the ZT of the Ti_1-Nb(FeCoNi)Sb samples were significantly increased. The average ZT values of the Nb-doped pseudo-ternary half-Heusler samples were dozens of times that of the TiCoSb prepared using the same process.