Effects of Surface Treatment Method Forming New Nano/Micro Hierarchical Structures on Attachment and Proliferation of...

Titanium (Ti) and Ti-based alloys are commonly used in dental implants, and surface modifications of dental implants are important for achieving osseointegration (i.e., direct connection between the implant surface and bone). This study investigated the effect of an eco-friendly etching solution-a hydrogen peroxide-sodium bicarbonate mixture-on the surface properties and contact angles of osteoblast adhesion and proliferation on Ti surfaces. Disk-shaped Ti specimens were prepared using different surface treatments (machining, sandblasting, and sandblasting/acid-etching), and they were immersed in the etching solution and ultrasonically cleaned. Surface characterization was performed using scanning electron microscopy, digital microscopy, contact angle analysis, and X-ray photoelectron spectroscopy. MG-63 osteoblasts were cultured on the specimens, and their adhesion to the specimen surface and proliferation were examined using staining and the MTT assay, respectively. Additional etching with the etching solution caused the formation of nano/micro hierarchical structures, increased surface roughness, and enhanced hydrophilicity. Osteoblast adhesion and proliferation were found to improve on the modified surfaces. The eco-friendly etching method has the potential to enhance the biological properties of Ti implant surfaces and thereby improve dental implant performance.