Fatigue behaviour of a self-healing dental composite

Novel self-healing resin-based composites containing microcapsules have been developed to improve the mechanical performance of dental restorations. However, the long-term fatigue behaviour of these self-healing composites has still been hardly investigated. Therefore, this manuscript studied the fatigue behaviour of self-healing composites containing microcapsules by subjecting the specimens to traditional staircase tests and ageing in a custom-designed chewing simulator (Rub&Roll) to simulate oral ageing physiologically relevant conditions.

To prepare self-healing composite, poly(urea-formaldehyde) microcapsules containing acrylic self-healing liquids were synthesized. Subsequently, these microcapsules (10 wt%) and initiator (benzoyl peroxide, BPO, 2 wt%) were incorporated into a commercial flowable resin-based composite. Microcapsule-free resin-based composites with and without BPO were also prepared as control specimens. A three-point flexural test was used to measure the initial flexural strength (S_initial). Subsequently, half of the specimens were used for fatigue testing using a common staircase approach to measure the fatigue strengths (FS). In addition, the other specimens were aged in the Rub&Roll machine for four weeks where after the final flexural strength (S_final) was measured.

Compared to S_initial, FS of all tested specimens significantly decreased as measured through staircase testing. After 4 weeks of ageing in the Rub&Roll machine, S_final was significantly reduced compared to S_initial for microcapsule-free resin-based composites, but not for the self-healing composites (p = 0.3658). However, the self-healing composites are still in the experimental phase characterized by a low mechanical strength, which still impedes further clinical translation.

Self-healing composites containing microcapsules exhibit improved fatigue resistance compared to microcapsule-free non-self-healing composites.