Enhancing potassium ions adsorption on mesoporous carbon spheres with abundant internal surface via engineering...

Mesoporous carbon spheres (MCSs) show great potential for using as high-performance anodes in potassium-ion batteries (PIBs). Design and synthesis of MCSs with suitable multiscale structures and heteroatom doping or co-doping in MCSs are successfully employed to optimize the ion and electron transportation, however, it is still a challenge to explore MCS-based anodes with satisfactory potassium storage performance. In this work, we report novel S-doped MCS samples with abundant internal surfaces for potassium storage. The S doping sites are controlled during the synthesis, and the effect of different doping sites on the potassium storage is systematically studied. It is found that S doping between the carbon layers enlarges interlayer spacing and facilitates potassium ion adsorption. Consequently, the optimized sample shows an excellent rate capability of 144 mAh/g at 5.0 A/g, and a high reversible specific capacity of 325 mAh/g after 100 cycles at 0.1 A/g with a capacity retention of 91.2%. The important role of element doping sites on ion adsorption and ion storage performance is confirmed by theoretical investigations. Controlling the doping sites in MCSs provides a new approach to designing high-performance electrodes for energy storage and conversion applications.