Kinetically well-matched porous framework dual carbon electrodes for high-performance sodium-ion hybrid capacitors

Sodium-ion hybrid capacitors (SIHCs) have attracted extensive interest due to their applications in sodium-ion batteries and capacitors, which have been considered expectable candidates for large-scale energy storage systems. The crucial issues for achieving high-performance SIHCs are the reaction kinetics imbalances between the slow Faradic battery-type anodes and fast non-Faradaic capacitive cathodes. Herein, we propose a simple self-template strategy to prepare kinetically well-matched porous framework dual-carbon electrodes for high-performance SIHCs, which stem from the single precursor, sodium ascorbate. The porous framework carbon (PFC) is obtained by direct calcination of sodium ascorbate followed by a washing process. The sodium-ion half cells with PFC anodes exhibit high reversible capacity and fast electrochemical kinetics for sodium storage. Moreover, the as-obtained PFC can be further converted to porous framework activated carbon (PFAC) with rich porosity and a high specific surface area, which displays high capacitive properties. By using kinetically well-matched battery-type PFC anodes and capacitive PFAC cathodes, dual-carbon SIHCs are successfully assembled, which can work well in 0-4 V. The optimal PFC//PFAC SIHC exhibits high energy density (101.6 Wh kg^-1 at 200 W kg^-1), power density (20 kW kg^-1 at 51.1 Wh kg^-1), and cyclic performance (71.8 % capacitance attenuation over 10,000 cycles).