Interaction pathways of implant metal localized corrosion and macrophage inflammatory reactions

Macrophages play a central role in immunological responses to metallic species associated with the localized corrosion of metallic implants, and mediating in peri-implant inflammations. Herein, the pathways of localized corrosion-macrophage interactions were systematically investigated on 316L stainless steel (SS) implant metals. Electrochemical monitoring under macrophage-mediated inflammatory conditions showed a decreased pitting corrosion resistance of 316L SSs in the presence of RAW264.7 cells as the cells would disrupt biomolecule adsorbed layer on the metal surface. The pitting potentials were furtherly decreased when the RAW264.7 cells were induced to the M1 pro-inflammatory phenotype by the addition of lipopolysaccharide (LPS), and pitting corrosion preferentially initiated at the peripheries of macrophages. The overproduction of aggressive ROS under inflammatory conditions would accelerate the localized corrosion of 316L SS around macrophages. Under pitting corrosion condition, the viability and pro-inflammatory polarization of RAW264.7 cells were region-dependent, lower viability and more remarkable morphology transformation of macrophages in the pitting corrosion region than the pitting-free region. The pitting corrosion of 316L SS induced high expression of CD86, TNF-α, IL-6 and high level of intracellular ROS in macrophages. Uneven release of metallic species (Fe²⁺, Cr³⁺, Ni²⁺, etc) and uneven distribution of surface overpotential stimulated macrophage inflammatory responses near the corrosion pits. A synergetic effect of localized corrosion and macrophages was revealed, which could furtherly promote localized corrosion of 316L SS and macrophage inflammatory reactions. Our results provided direct evidence of corrosion-macrophage interaction in metallic implants and disclosed the pathways of this mutual stimulation effect.