Surface-structure tailoring of Dendritic PtCo nanowires for efficient oxygen reduction reaction

Platinum-based alloy nanowire catalysts demonstrates great promise as electrocatalysts to facilitate the cathodic oxygen reduction reaction (ORR) of proton exchange membrane fuel cells (PEMFCs). However, it is still challenge to further improve the Pt atom utilization of Pt based nanowires featuring inherent structural stability. Herein, a new structure of PtCo nanowire with nanodendrites was developed using CO-assistance solvent thermal method. The dendrite structure with an average length of about 7 nm are characterized by a Pt-rich surface and the high-index facets of {533}, {331} and {311}, and grows from the ultra-fine wire structure with an average diameter of about 3 nm. PtCo nanowires with nanodendrites developed in this work shows outstanding performance for ORR, in which its mass activity of 1.036 A/mg_Pt is 5.76 times, 1.74 times higher than that of commercial Pt/C (0.180 A/mg_Pt) and PtCo nanowires without nanodendrites (0.595 A/mg_Pt), and its mass activity loss is only 18% under the accelerated durability tests (ADTs) for 5k cycles. The significant improvement is attributed to high exposure of active sites induced by the dendrite structure with Pt-rich surface with the high-index facets and Pt-rich surface. This structure may provide a new idea for developing novel 1D Pt based electrocatalysts.