Oxidation of Ceramic Materials Based on HfB₂-SiC under the Influence of Supersonic CO₂ Jets and Additional Laser...

The features of oxidation of ultra-high-temperature ceramic material HfB₂-30 vol.%SiC modified with 1 vol.% graphene as a result of supersonic flow of dissociated CO₂ (generated with the use of high-frequency induction plasmatron), as well as under the influence of combined heating by high-speed CO₂ jets and ytterbium laser radiation, were studied for the first time. It was found that the addition of laser radiation leads to local heating of the central region from ~1750 to ~2000-2200 °C; the observed temperature difference between the central region and the periphery of ~300-550 °C did not lead to cracking and destruction of the sample. Oxidized surfaces and cross sections of HfB₂-SiC-C_G ceramics with and without laser heating were investigated using X-ray phase analysis, Raman spectroscopy and scanning electron microscopy with local elemental analysis. During oxidation by supersonic flow of dissociated CO₂, a multilayer near-surface region similar to that formed under the influence of high-speed dissociated air flows was formed. An increase in surface temperature with the addition of laser heating from 1750-1790 to 2000-2200 °C (short term, within 2 min) led to a two to threefold increase in the thickness of the degraded near-surface area of ceramics from 165 to 380 microns. The experimental results indicate promising applications of ceramic materials based on HfB₂-SiC as part of high-speed flying vehicles in planetary atmospheres predominantly composed of CO₂ (e.g., Venus and Mars).